H050Mn is recommended for Injection Moulding and is an ideal choice as a compounding base and blending material in the compound. It is also suitable for moulding rigid containers, housewares and thermos wares. Reliance Pp Injection Moulding 5 MFI H050Mn contains a nucleating agent for high rigidity, reduced cycle time and antistatic agent that reduces static charge build-up in products.
Typical Characteristics
| Property | Test Method | Unit | Typical Value** |
| Melt Flow Rate (230°C/2.16 kg) | ASTM D1238 | g/10 min | 3.4 |
| Tensile Strength at Yield (50 mm/min) | ASTM D638 | MPa | 36 |
| Elongation Yield (50 mm/min) | ASTM D638 | % | 10 |
| Flexural Modulus (1% secant) | ASTM D790A | MPa | 1750 |
| Notched Izod Impact Strength (23°C) | ASTM D256 | J/m | 35 |
| Heat Deflection Temperature (455 kPa) | ASTM D648 | °C | 110 |
- Typical values not to be taken as specifications. Al the mechanical properties as per ASTM D638 Type I specimen injection moulded in accordance with ASTM D4101.
Applications:
- Furniture And rigid packaging
Regulatory Information
- Meets the requirements stipulated in ISA 10910 on 'Specification for Polypropylene and its copolymers for safe use in contact with foodstuff, pharmaceuticals and drinking water. Additives incorporated in this grade conform to the positive list of constituents as prescribed in IS 10909. The grade and the additives incorporated in it also comply with the FDA: CFR 21,177,1520 Olefin polymers.
Storage Recommendations
- Bags should be stored in dry/closed conditions at temperatures below 50 C and protected from UV/ direct sunlight