Reliance PPCP Injection Moulding 8 MFI

Company : Raychand Enterprise   |   Raw Material / Re Processed / PPCP Granules

Reliance PPCP Injection Moulding 8 MFI

Product Code: RECY-RA-RE-692
Company: Raychand Enterprise

Packaging Type: PVC Bag
Usage: Furniture and Industrial Products
Brand: Reliance
Packaging Size: 25 Kg
Physical State: Granules

Location: Ahmedabad, Gujarat

Enquire Now


Reliance PPCP Injection Moulding 8 MFI C080MA is recommended for use in Injection Molding processes where high impact strength is required. It is an ideal material to use in making furniture & industrial products. Reliance PPCP Injection Moulding 8 MFI  C080MA contains an antistatic agent that reduces static charge build-up in products.

Typical Characteristics

Property Test Method Unit Typical Value**
Melt Flow Rate (230°C/2.16 kg) ASTM D1238 g/10 min 9
Tensile Strength at Yield (50mm/min) ASTM D638 MPa 23
Elongation at Yield (50mm/min) ASTM D638 % 7
Flexural Modulus (1% secant ) ASTM D790A MPa 1000
Notched Izod Impact strength (23°C) ASTM D256 J/m 150
Heat Deflection Temperature (455 kPa) ASTM D648 °C 95

  • Typical values, not to be taken as specifications. All the mechanical properties as per ASTM D638 Type I specimen injection moulded in accordance with ASTM D4101


  • Furniture, pails and industrial products

Regulatory Information

  • Meets the requirements stipulated in IS 10910 on ‘Specification for Polypropylene and its Copolymers for safe use in contact with foodstuff, pharmaceuticals, and drinking water’. Additives incorporated in this grade conform to the positive list of constituents as prescribed in IS 10909. The grade and the additives incorporated in it also comply with the FDA:CFR Title 21,177.1520, Olefin polymers

Storage Recommendations

  • Bags should be stored in dry/closed conditions at temperatures below 50°C and protected from UV / direct sunlight


Hindustan Plastics - HPMC - Extrusion Redefined
Laxmi Plastic
Roadmap for EPR Implementation of Plastics in India


News Updates